ARGOCOLA ELITE 400 RAPIDO
High-performance cementitious adhesive C2FTES1
Colors:
Grey
25Kg - 350010
ARGOCOLA ELITE 400 is a high performance cementitious adhesive C2FTES1 formulated with special cements, selected aggregates, organic additives and polymers that give it an extraordinary capacity for deformation, adhesion and durability for a fast start-up.
Installation video
Descriptive Memory
- Ceramic tiles shall be laid with ARGOCOLA ELITE 400 cementitious adhesive, made by the company Argos derived from cement, class C2FTE S1 according to the UNE EN 12004 standard. The fixing substrate shall be sound, clean, free of friable parts, completely hardened and shall have completed its time of dimensional variation. The joints shall be respected. Ceramic tiles shall be laid with spacers for tile-to-tile joints.
Instruction for Use
- Mix ARGOCOLA ELITE 400 with 7.5 L of clean water per 25 kg bag manually or mechanically until a homogeneous, creamy and lump-free mixture is obtained.
- Allow to stand for 5 minutes before application.
- Comb the adhesive onto the substrate with a 6×6 mm notched trowel for small formats or 8×8 mm for formats larger than 40×40 cm. The adhesive is spread out in layers of approx. 1 m² so that the time that elapses between the application of the adhesive on the substrate and the laying of the tiles does not cause the adhesive to lose sufficient wettability for proper adhesion.
- The tiles should be pressed until the grooves of the adhesive are flattened.
Cleaning of Work Tools
- Fresh product, with water.
- Dry product, scraping.
Presentation
- Weight (kg): 25
- Yield (kg/m²): 4.5
- Performance in mm thickness (kg/m²): 1,8
- Appearance: Powder
- Colour: Grey
- Product code: 350010
Technical Data
| Concept | Value | Standard |
|---|---|---|
| Mass per unit area (nominal) (kg/m²) | 25 | - |
| Capillary Absorption (kg/m²h0.5) | W2 | - |
| Adhesion after heat (N/mm²) | ≥ 1,0 | - |
| Initial adhesion (N/mm²) | ≥ 1,0 | - |
| Initial adhesion before 6 hours (N/mm²) | 0.5 | - |
| Adhesion after freeze-thaw cycles (N/mm²) | ≥ 1,0 | - |
| Adhesion after immersion in water (N/mm²) | ≥ 1,0 | - |
| Adhesion after open time 30 min (N/mm²) | ≥ 0,5 | - |
| Mixing water (%) | 24/26 | - |
| Classification according to UNE EN 12004 | C2FTES1 | - |
| Transverse strain (mm) | ≥ 2,5 | - |
| Bulk density (kg/L)v ~ Value | 1,60 ± 0,05 | - |
| Fresh mass density (kg/L) ~ Value | 1,80 ± 0,05 | - |
| Slipping (mm) | ≤ 0,5 | - |
| Grain size range (mm) ~ value | 0/0,8 | - |
| Water vapour permeability (µ) | Clase I | - |
| Reaction to fire | A1 | - |
| Joint filling (hours) | 6 | - |
| Hazardous substances | Ver HS | - |
| Parts setting time (min) | 15 | - |
| Mixture lifetime (min) | 30 | - |
Addtitional Technical Data