DANOCRET PROTECT 100

Mortar for waterproofing and protection of concrete structures. Monocomponent

Product variations:
Waterproofing
EPD S-P-03332 EPD S-P-03332
DANOCRET PROTECT 100 is a thixotropic, single-component, polymer modified mortar (PCC) for the surface protection and waterproofing of concrete, formulated on the basis of a mixture of hydraulic binders, selected aggregates and polymers that provide excellent adherence and waterproofing capacity.

Descriptive Memory

The surface protection and waterproofing of the concrete without movement will be carried out with the single-component, thixotropic, polymer modified mortar DANOCRET PROTECT 100 of the company DANOSA, according to the UNE EN 1504-2 standard, in accordance with principle 1 (method 1.3) and principle 2 (method 2.2.) of the UNE EN 1504-9 standard.

Instruction for Use

Mix DANOCRET® PROTECT 100 with 6.0 L of clean water per bag of 25 kg preferably by mechanical means until a homogeneous, creamy and lump-free mixture is obtained with a thick paint consistency. Apply the mortar manually with a trowel in thicknesses between 2 and 4 mm, pressing the mortar with the trowel on the support. The application time is 10-20 minutes depending on environmental conditions.

Cleaning of Work Tools

  • If the product is fresh, with water
  • If the product is dry, scraping

Presentation

  • Weight (kg): 25
  • Yield (kg/m²): 3
  • Performance in mm thickness (kg/m²): 1,8
  • Appearance: Powder
  • Colour: Grey
  • Product code: 350136
DANOCRET PROTECT 100

Technical Data

Concept Value Standard
Mass per unit area (nominal) (kg/m²) 25 -
Capillary Absorption (kg/m²h0.5) ≤ 1,00 EN 1062-3:2008
Adhesion after heat (N/mm²) ≥ 0,5 -
Initial adhesion (N/mm²) ≥ 0,5 -
Adhesion after freeze-thaw cycles (N/mm²) ≥ 0,5 -
Adhesion after thermal compatibility (N/mm²) ≥ 1,00 EN 13687-1 y 2
Adhesion after immersion in water (N/mm²) ≥ 0,5 -
Adhesion after immersion in water with lime (N/mm²) ≥ 0,5 -
Direct Tensile Adhesion (N/mm²) ≥ 1,00 EN 1542:1999
Mixing water (%) 23 -
Crack elongation capacity (mm) 0.25 (capa de 2 mm a 23 °C) EN 14891 Apdo. A.8.2
Classification according to EN 14891 Table 4 MC -
Bulk density (kg/L)v ~ Value 1,50 ± 0,05 -
Fresh mass density (kg/L) ~ Value 1,80 ± 0,05 -
Maximum thickness (mm) 3 -
Minimum thickness (mm) 2 -
Thickness per layer Nunca superior a 2 kg/m² -
Water impermeability cumple -
Grain size range (mm) ~ value 0/0,8 -
Water vapour permeability (µ) Clase I -
pH 10.5 ± 0.5 -
Reaction to fire A1 -
Compacting resistence 28 days (N/mm²) 20 -
Resistance to fissure cracking at 0 ºC A2 EN 1062-7:2008
Hazardous substances Ver HS -

Addtitional Technical Data

CO2 permeability Clase III EN 1062-6:2003