GLASDAN 30 P POL
APP plastomeric 3 kg/m² underlay. Torch applied.
Product variations:
GLASDAN 30 P POL is a waterproofing bituminous sheet with non self-protected surface of 3.0 kg/m². Composed of a fibreglass reinforcement and covered on both sides with polymer modified bitumen mastic. A polyethylene film is used as anti-adherent material on both sides. Tested according to standard EN test methods.
Instruction for Use
Substrate Preparation: The base surface must be clean, dry and free of debris to provide maximum adhesion. A bituminous primer may be needed depending upon the condition of the substrate. We recommend Curidan, Impridan 100, Maxdan or Maxdan Caucho. In case of non-porous substrates we recommend that a test application is made to ensure correct adhesion. In case of thermal insulations boards a primer is not necessary.
Product application:Â For ease of installation, it is recommended to cut rolls into smaller and more manageable size. Remove the release liner and install whilst applying pressure onto the surface. Start from the center and spread to the outside edges. The use of a roller is recommended to improve adhesion.
Product application:Â For ease of installation, it is recommended to cut rolls into smaller and more manageable size. Remove the release liner and install whilst applying pressure onto the surface. Start from the center and spread to the outside edges. The use of a roller is recommended to improve adhesion.
Maintenance Recommendations
- Please refer to DANOSA UK Technical Statement ‘Flat Roof Waterproofing – Cleaning and Maintenance Recommendations’
Presentation
- Length (cm): 1200
- Width (cm): 100
- Thickness (mm): 2.5
- Surface (m²): 12
- Product code: 141622
Technical Data
| Concept | Value | Standard |
|---|---|---|
| Mass per unit area (nominal) (kg/m²) | 3 | - |
| Density (kg/m³) | 1200 | - |
| External fire behaviour | Broof(t1) | UNE-EN 1187; UNE-EN 13501-5 |
| Durability flexibility | -5 ± 5 | - |
| Creep durability (ºC) | 120 ±10 | UN-EN 1110 |
| Elongation at break longitudinal (%) | NPD | UNE-EN 12311-1 |
| Elongation at transverse break (%) | NPD | UNE-EN 12311-1 |
| Watertightness at 10 kPa (Type A) | Pasa | UNE-EN 1928 |
| Water vapour resistance factor (μ) | >100.000 | UNE-EN 1931 |
| Low temperature flexibility (ºC) | <-15 | UNE-EN 1109 |
| Reaction to fire | E | UNE-EN 11925-2; UNE-EN 13501-1 |
| Resistance to static loading (kg) | NPD | UNE-EN 12730 |
| Resistance to root penetration | No Pasa | EN 13948 |
| Longitudinal tensile strength (N / 5cm) | 350 ± 100 | UNE-EN 12311-1 |
| Transverse tensile strength (N / 5cm) | 250 ± 100 | UNE-EN 12311-1 |
| Longitudinal resistance to tearing (nail shank) (N) | PND | UNE-EN 12310-1 |
| Transversal resistance to tearing (nail shank) (N) | PND | UNE-EN 12310-1 |
| Resistance to impact, A (mm) | NPD | UNE-EN 12691 |
| Joint Strength: Welding Shear | NPD | UNE-EN 12317-1 |
| Hazardous substances | PND | - |
Addtitional Technical Data
Environmental Information
| Concept | Value | Standard |
|---|---|---|
| Volatile organic compounds (COV's) (µg/m³) | 50 (A+) | ISO 16000-6:2006 |
| Post-consumer recycled content (%) | 35 | - |
| Manufactured in | Fontanar - Guadalajara (España) | - |