POLYDAN PRO 60/GP.

High-quality SBS elastomeric 5,6 kg/m² capping sheet. Torch Applied.

Product variations:
Waterproofing
BBA 10/4787 (PS1) BBA 10/4787 (PS1)
High quality bituminous SBS modified capsheet reinforced with a heavy non-woven polyester felt. The upper surface is finished with mineral chippings. The underside has a quick-melt thermofusible film. Designed for torch-applied applications and Safe2Torch details using hot-air welding.

Scope

  • Capsheet in multi-layer waterproofing systems.
  • Capsheet in multi-layer systems with heavy protection.
  • Capsheet in single-layer waterproofing systems.

Advantages & Benefits

  • Long life expectancy.
  • High dimensional stability.
  • High tensile strength and high elongation at break.
  • High resistance to tearing.
  • High resistance to static and dynamic piercing.
  • Total impermeability to water and water vapour.
  • Rot-proof.
  • Very stable in the long term.

Support

  • On suitable underlays or self-protected bonded protection.
  • Compatible thermal insulation products.
  • Concrete subsrates.
  • Mortar subsrates.

Instruction for Use


  • Substrate should be dry and clean from grease, dirt, debris or any other contaminants.
  • Where applicable, prime surface with CURIDAN or BITUMEN PRIMER+ in accordance with DANOSA instructions and allow to dry.
  • For field applications:
  • The membrane should be laid along the same direction as the underlay membrane, offset by a minimum of 300mm to ensure sufficient staggering of laps between layers.
  • Roll the membrane into position, allowing for 80mm side overlaps and100mm head overlaps and cut to length. All overlaps and cross joints should be staggered by a minimum of 300mm. Overlaps and cross joint.
  • Using a length of 100mm ø pipe (cut fractionally short of roll width) as an insert tube, roll back the membrane for a portion of the length (approximately 50%).
  • Heat activate the membrane by torching in a vee area between the roll and substrate.
  • Roll can be pushed forward by foot or by other suitable equipment. Apply downwards pressure when moving the roll to extrude a molten bead of bitumen from edges.
  • For detail applications
  • The membrane should be laid along the same direction as the underlay membrane, offset by a minimum of 300mm to ensure sufficient staggering of laps between layers.
  • The membrane must be installed a minimum of 150mm above the finished surface of the system.
  • Place the membrane into position, allowing for 80mm side overlaps and100mm head overlaps and cut to length ensuring all overlaps and cross joints are staggered by a minimum of 300mm.
  • Heat activate the membrane by torching between the membrane and substrate.
  • Apply pressure and consolidate the bond to the substrate, ensuring a molten bead of bitumen is extruded from the edges.


    • Where falls apply, membrane rolls should be rolled up the slope so that water drains over and not into membrane overlaps.

    Indications and Important Recommendations

    • In the case of new construction and renovation work, the possible chemical incompatibilities with SBS elastomer-modified bitumen sheets must be taken into account.
    • In case of refurbishment, chemical incompatibilities with old waterproofing systems consisting of PVC membranes, modified tar-based mastics or any other, shall be taken into account, and it may be necessary to remove them completely or to use suitable separating layers.
    • If it is necessary to adhere to metallic or slightly porous elements, a bituminous primer (IMPRIDAN 100) shall be applied to the entire surface to be welded beforehand.
    • On exposed self-protected roofs, occasional water retention that could lead to sediment accumulation and damage to the waterproofing membrane shall be avoided.
    • This product may form part of a waterproofing system, so all the documents referred to in the Danosa Solutions Manual must be taken into account, as well as all the regulations and legislation that must be complied with in this respect.
    • Certain precautions must be taken when pouring the asphalt agglomerate if it is poured directly on top of the waterproofing.
    • The asphalt paver shall be wheeled and, if tracked, shall be fitted with rubber pads.
    • The asphalt agglomerate shall be laid at temperatures between 130ºC and 180ºC.
    • Self-protected sheets in coloured mineral or ceramic granules may have different colour shades depending on the different production batches. The mineral granule may darken naturally over time.
    • There is no chemical incompatibility between the Danosa range of SBS elastomeric bitumen and APP plastomeric bitumen membranes.
    • Access walkway membranes are available for roof areas with heavy foot traffic.
    • Not suitable as cap sheet on green roofs; use GARDEN variant.
    • A separating layer (DANOFELT or DANODREN) shall be laid before laying the heavy protection (paving, gravel, topsoil, etc.), except in the case of asphalt paving which is poured directly on the waterproofing.
    • Special attention must be paid to the execution of the singular points, such as parapets (meetings with vertical and emergent elements), drains, expansion joints, etc.
    • Polyurethane foam shall not be sprayed directly on top of the waterproofing without the use of a suitable separating layer (geotextiles, mortar layers, polyethylene film, etc).
    • NOTE: For more information on the Danosa systems in which this product is used, please see the document "Waterproofing Solutions".

    Maintenance Recommendations

    • Please refer to DANOSA UK Technical Statement ‘Flat Roof Waterproofing – Cleaning and Maintenance Recommendations’

    Warning

    • Do not apply on wet or frozen surfaces.

    Handling, storage and preservation

    • Before moving the pallet, check the condition of the shrink-wrap and reinforce if necessary.
    • The product must be stored in a dry place protected from rain, sun, heat and low temperatures.
    • The product must be stored in an upright position.
    • Handle with a crane with a protective net.
    • Pallets shall not be stacked on top of each other.

    Notice

    • The information contained in this document and any other advice provided, are given in good faith, based on DANOSA's current knowledge and experience when products are properly stored, handled and applied, in normal situations and in accordance with the recommendations of DANOSA. The information applies only to the application (s) and the product (s) to which reference is expressly made. In case of changes in the parameters of the application, or in case of a different application, consult the DANOSA Technical Service before using the DANOSA products. The information contained herein does not exonerate the responsibility of the building agents to test the products for the application and intended use, as well as their correct application in accordance with current legal regulations. The product images used in our communications are indicative and may differ slightly in color and aesthetic appearance in relation to the final product.Orders are accepted in accordance with the terms of our current General Sales Conditions.DANOSA reserves the right to modify, without prior notice, the data reflected in this documentation.Website: www.danosa.com E-mail: info@danosa.com Telephone: +34 949 88 82 10

    Presentation

    • Length (cm): 800
    • Width (cm): 100
    • Thickness (mm): 3.9 (Overlap)
    • Colour: Black
    • Product code: 141124
    POLYDAN PRO 60/GP.

    Technical Data

    Concept Value Standard
    Mass per unit area (nominal) (kg/m²) 5.6 -
    Density (kg/m³) 1436 -
    Thermal compatibility. Part I. (N/mm²) >3,5E-09 -
    External fire behaviour Broof (t1, t4) UNE-EN 1187; UNE-EN 13501-5
    Durability flexibility -10 ± 5 -
    Creep durability (ºC) 100 ±10 UN-EN 1110
    Elongation at break longitudinal (%) 45 ±15 UNE-EN 12311-1
    Elongation at transverse break (%) 45 ±15 UNE-EN 12311-1
    Watertightness at 10 kPa (Type A) Pasa UNE-EN 1928
    Watertightness at 300 kPa Pasa UNE-EN 1928
    Water vapour resistance factor (μ) >20.000 UNE-EN 1931
    Low temperature flexibility (ºC) <-25 UNE-EN 1109
    Reaction to fire E UNE-EN 11925-2; UNE-EN 13501-1
    Resistance to static loading (kg) >20 UNE-EN 12730
    Resistencia a la difusión (GPa.s.m²/kg) 500 ± 50 -
    Resistance to root penetration No Pasa UNE-EN 13948
    Longitudinal tensile strength (N / 5cm) 900 ± 250 UNE-EN 12311-1
    Transverse tensile strength (N / 5cm) 650 ± 250 UNE-EN 12311-1
    Longitudinal resistance to tearing (nail shank) (N) PND UNE-EN 12310-1
    Transversal resistance to tearing (nail shank) (N) PND UNE-EN 12310-1
    Resistance to impact, A (mm) >1000 UNE-EN 12691
    Resistance to impact, B (mm) >1500 -
    Joint Strength: Welding Shear 650 ± 250 UNE-EN 12317-1
    Hazardous substances NPD -

    Addtitional Technical Data

    Dimensional stability at elevated temperatures (longitudinal) (%) <0.5 UNE-EN 1107-1 Dimensional stability at high temperatures (transversal) (%) <0.5 UNE-EN 1107-1 Dimensional stability at elevated temperatures (longitudinal) (%) <0.5 UNE-EN 1107-1 Dimensional stability at high temperatures (transversal) (%) <0.5 UNE-EN 1107-1 Creep resistance at high temperatures (ºC) >100 UN-EN 1110

    Standards and Certification

    • In accordance with the UNE-EN 13707 standard ‘Flexible sheets for waterproofing - Reinforced bitumen sheets for roof waterproofing - Definitions and characteristics’.
    • In accordance with the UNE-EN 13969 standard for ‘Flexible sheets for waterproofing - Bitumen damp proof sheets including bitumen basement tanking sheets - Definitions and characteristics’.

    Environmental Information

    Concept Value Standard
    Volatile organic compounds (COV's) (µg/m³) 50 (A+) ISO 16000-6:2006
    Post-consumer recycled content (%) 35 -