ARGOCOLA ELITE 300
High performance cementitious adhesive C2TE
Colors:
White
25Kg - 350007
Grey
25Kg - 350008
ARGOCOLA ELITE 300 is a high performance C2TE cementitious adhesive formulated with Portland cement, selected aggregates, organic additives and polymers that give it extraordinary workability and adhesion.
Installation video
Advantages & Benefits
- High mechanical performance.
- Long shelf-life, even after opening.
- Great bonding.
- Great plasticity.
- Allows for rectification of pieces.
- Without off-hook.
Descriptive Memory
Ceramic tiles shall be laid with ARGOCOLA ELITE 300 cementitious adhesive, made by the company Argos derived from cement, class C2TE according to the UNE EN 12004 standard. The fixing substrate shall be sound, clean, free of friable parts, completely hardened and shall have completed its time of dimensional variation. The joints shall be respected. Ceramic tiles shall be laid with spacers for tile-to-tile joints.
Instruction for Use
- Mix ARGOCOLA ELITE 300 with 6.75 L of clean water per 25 kg bag manually or mechanically until a homogeneous, creamy and lump-free mixture is obtained.
- Allow to stand for 5 minutes before application.
- Comb the adhesive onto the substrate with a 6×6 mm notched trowel for small formats or 8×8 mm for formats larger than 40×40 cm. The adhesive is spread out in layers of approx. 1 m² so that the time that elapses between the application of the adhesive on the substrate and the laying of the tiles does not cause the adhesive to lose sufficient wettability for proper adhesion.
- The tiles should be pressed until the grooves of the adhesive are flattened.
Cleaning of Work Tools
-Fresh product, with water
- Dry product, scraping
Presentation
- Weight (kg): 25
- Yield (kg/m²): 4,5
- Performance in mm thickness (kg/m²): 1,8
- Appearance: Powder
- Colour: White
- Product code: 350007
Technical Data
| Concept | Value | Standard |
|---|---|---|
| Mass per unit area (nominal) (kg/m²) | 25 | - |
| Capillary Absorption (kg/m²h0.5) | W2 | - |
| Adhesion after heat (N/mm²) | ≥ 1,0 | - |
| Initial adhesion (N/mm²) | ≥ 1,0 | - |
| Adhesion after freeze-thaw cycles (N/mm²) | ≥ 1,0 | - |
| Adhesion after immersion in water (N/mm²) | ≥ 1,0 | - |
| Adhesion after open time 30 min (N/mm²) | ≥ 0,5 | - |
| Mixing water (%) | 24/26 | - |
| Classification according to UNE EN 12004 | C2TE | - |
| Bulk density (kg/L)v ~ Value | 1,60 ± 0,05 | - |
| Fresh mass density (kg/L) ~ Value | 1,80 ± 0,05 | - |
| Slipping (mm) | ≤ 0,5 | - |
| Grain size range (mm) ~ value | 0/0,8 | - |
| Water vapour permeability (µ) | Clase I | - |
| Reaction to fire | A1 | - |
| Joint filling (hours) | 24 | - |
| Hazardous substances | Ver HS | - |
| Parts setting time (min) | 30 | - |
| Mixture lifetime (min) | 120 | - |