ARGOCOLA ELITE 600
Highly deformable cementitious high performance cementitious adhesive C2TES2

Colors:
White
25Kg - 350197
ARGOCOLA ELITE 600 is a high performance deformable cementitious adhesive C2TES2 formulated with Portland cement, selected aggregates, organic additives and polymers that give it an extraordinary capacity for deformation, adhesion and durability.
Installation video

Advantages & Benefits
- High mechanical performance.
- Long shelf-life, even after opening.
- Great bonding.
- Great plasticity.
- Very deformable.
- Allows for rectification of pieces.
Descriptive Memory
- Ceramic tiles shall be laid with ARGOCOLA ELITE 600 deformable adhesive, made by the company Argos derived from cement, class C2FTE S2 according to the UNE EN 12004 standard. The fixing substrate shall be sound, clean, free of friable parts, completely hardened and shall have completed its time of dimensional variation. The joints shall be respected. Ceramic tiles shall be laid with spacers for tile-to-tile joints.
Instruction for Use
- Mix ARGOCOLA ELITE 600 with 7.0 L of clean water per 25 kg bag manually or mechanically until a homogeneous, creamy and lump-free mixture is obtained.
- Allow to stand for 5 minutes before application.
- Comb the adhesive onto the substrate with a 6×6 mm notched trowel for small formats or 8×8 mm for formats larger than 40×40 cm. The adhesive is spread out in layers of approx. 1 m² so that the time that elapses between the application of the adhesive on the substrate and the laying of the tiles does not cause the adhesive to lose sufficient moisture for proper adhesion.
- The tiles must be pressed until the grooves of the adhesive are flattened.
Cleaning of Work Tools
- Fresh product, with water.
- Dry product, scraping.
Presentation
- Weight (kg): 25
- Yield (kg/m²): 4.5
- Performance in mm thickness (kg/m²): 1,8
- Appearance: Powder
- Colour: White
- Product code: 350197

Technical Data
Concept | Value | Standard |
---|---|---|
Mass per unit area (nominal) (kg/m²) | 25 | - |
Capillary Absorption (kg/m²h0.5) | W2 | - |
Adhesion after heat (N/mm²) | ≥ 1,0 | - |
Initial adhesion (N/mm²) | ≥ 1,0 | - |
Adhesion after freeze-thaw cycles (N/mm²) | ≥ 1,0 | - |
Adhesion after immersion in water (N/mm²) | ≥ 1,0 | - |
Adhesion after open time 30 min (N/mm²) | ≥ 0,5 | - |
Mixing water (%) | 24/26 | - |
Classification according to UNE EN 12004 | C2TES2 | - |
Transverse strain (mm) | ≥ 5,0 | - |
Bulk density (kg/L)v ~ Value | 1,60 ± 0,05 | - |
Fresh mass density (kg/L) ~ Value | 1,80 ± 0,05 | - |
Slipping (mm) | ≤ 0,5 | - |
Grain size range (mm) ~ value | 0/0,8 | - |
Water vapour permeability (µ) | Clase I | - |
Reaction to fire | A1 | - |
Joint filling (hours) | 24 | - |
Hazardous substances | Ver HS | - |
Parts setting time (min) | 30 | - |
Mixture lifetime (min) | 120 | - |