ARGONIV 020 ELITE
Self-levelling, fast drying paste for low thicknesses
Colors:
Grey
25Kg - 350019
5Kg - 350185
ARGONIV 020 ELITE is a self-levelling paste based on hydraulic binders, selected aggregates, polymers and chemical additives that give it extraordinary pumping and levelling properties as well as excellent mechanical properties in short times.
Installation video
Advantages & Benefits
- Exceptional ability to self-level.
- Suitable for aesthetic requirements.
- Low dynamic stress.
- High mechanical performance.
- Fast hardening without cracking.
- Thickness ≥ 2 mm.
- Dampness less than 3% after 48 hours.
- Interiors.
- No segregation (great robustness in the face of differences in the amounts of water).
- Surface suitable for covering with carpet, ceramic, paint, etc.
- Accessible at 5 hours.
Descriptive Memory
The levelling of the interior floor with a maximum thickness of 10 mm will be carried out with ARGONIV 020 ELITE dry mortar from the company Argos derived from cement, class CT C25 F7 according to the UNE EN 13813:2003 standard. The substrate must be sound, clean, free of friable parts, completely hardened and have completed its time of dimensional variation. The construction joints shall be respected.
Instruction for Use
- Mix ARGONIV 020 ELITE with 5 L of clean water per 25 kg bag, preferably by mechanical means, until a homogeneous, creamy and lump-free mixture is obtained.
- Pour the mixture onto the substrate until the required thickness is reached.
- Pass a horizontal bar to vibrate the material in order to allow the air trapped in the mortar to escape and complete the levelling process.
- Sand the surface and vacuum before the final coating if necessary.
Cleaning of Work Tools
-Fresh product, with water.
- Dry product, scraping.
Presentation
- Weight (kg): 25
- Yield (kg/m²): 18
- Performance in mm thickness (kg/m²): 1,8
- Appearance: Powder
- Colour: Grey
- Product code: 350019
Technical Data
| Concept | Value | Standard |
|---|---|---|
| Mass per unit area (nominal) (kg/m²) | 25 | - |
| Capillary Absorption (kg/m²h0.5) | W2 | - |
| Mixing water (%) | 19 | - |
| Fresh flow characteristics (mm) | ≤ 135 | - |
| Classification according to UNE EN 13813 | CT C35 F11 | - |
| Bulk density (kg/L)v ~ Value | 1,50 ± 0,16 | - |
| Fresh mass density (kg/L) ~ Value | 1,80 ± 0,16 | - |
| Minimum thickness (mm) | 2 | - |
| Grain size range (mm) ~ value | 0/0,3 | - |
| Water vapour permeability (µ) | Clase I | - |
| Reaction to fire | A1 | - |
| Compacting resistence 24 hours (N/mm²) | ≥ 15 | - |
| Compacting resistence 28 days (N/mm²) | ≥ 35 | - |
| Compacting resistence 5 hours (N/mm²) | ≥ 8 | - |
| Compacting resistence 7 days (N/mm²) | ≥ 11 | - |
| Flexural strength after 28 days (N/mm²) | ≥ 11 | - |
| Retraction at 28 days (mm/m) | ≤ 1 | - |
| Hazardous substances | Ver HS | - |
| Workability (min) | 30 | - |
| Trafficability (hours) | 5 | - |