DANOPOL+ HSF 1.5

Single Ply PVC-p 1.5 mm Fleecebacked membrane. Adhered.

Product variations:

BBA 14/5118 (3)

EPD S-P-00691

Datasheet

Declaration of Performance (DoP)

Description Technical features and measures Related documentation

1.5 mm PVC-P single ply membrane, reinforced with polyester net carrier and, a 300 g geotextile fleece bonded to the underside. Featuring a 6 cm overlap on its right longitudinal side, this product enables effortless overlaying and welding to the adjacent membrane. The DANOPOL "+" range has an enhanced formula with improved weather and UV radiation resistance properties. This formula also integrates a biocide that keeps the membrane protected against a wide range of harmful microorganisms.

Instruction for Use

The membrane should not be installed in adverse weather conditions. It must not be laid in rain, snow, or heavy fog, nor if the temperature falls below 5ºC, unless precautions against condensation have been taken.
Do not apply on wet or frozen surfaces.
Not suitable for pitched roofs over 5° (1:11) and/or vertical surfaces.
The membrane layers must always be installed with staggered overlaps and in such a manner that the laps fall in the direction toward the outlets.
The sheets shall be laid in such a way that no transverse overlap of each row is aligned with any of those of the adjoining rows.
The joint between sheets shall be made by thermoplastic hot-air welding.
Attachment of DANOPOL HSF membrane may be achieved by full bonding, or loose laid (ballasted) with guidance from DANOSA technical services; the choice should depend upon the type of substrate and the required resistance to wind uplift pressure.

For single layer application direct to deck:

The surface of the base substrate shall be resistant, uniform, smooth, clean, dry, and free of foreign bodies.
Before laying the waterproofing membrane, apply Fleecebond Adhesive to the entire surface of the substrate in accordance with the applicable datasheet instructions.
The membrane must terminate a minimum of 15cm above the surface of the finished roof surface level.
Finished edges must be terminated in accordance with DANOSA UK recommendations (see standard details).

For adhered applications:

Roll the DANOPOL or DANOPOL+ HSF 1.5 into position, allowing for 50mm side overlaps and 50mm head overlaps and cut to length. At perimeters and details, allow an additional 50mm to allow for mechanical restraint.
Apply DANOSA UK FLEECEBOND Adhesive (see DANOSA UK Technical Datasheet) to the substrate only in accordance with DANOSA UK instructions.
Position the next roll of DANOPOL or DANOPOL+ HSF 1.5, allowing for overlaps as previous, and seal with a minimum 30-40mm hot-air weld in accordance with DANOSA UK instructions.

The overlaps shall be at least 4cm 5 cm. and the welding of the lower sheet with the upper one shall be at least 4 cm. In the case of thermoplastic welding, immediately after welding, the joint shall be pressed with a roller, thus ensuring a homogeneous joint. To check the joints, a physical check shall be made using a blunt metal needle (with a rounded tip with a radius between 1mm and 3mm), passing it along the edge of the joint.
No more than three sheets shall be joined at a single point.
In T-joints (three sheets intersecting at one point), the bottom sheet shall be chamfered to prevent capillary leakage or be reworked with the hot air welder.
The apex of the angle formed by the transverse and longitudinal edges of the upper part shall be cut in the form of a curve.
For the transverse overlapping of sheets and if profiles are to be attached to the sheet, they shall be covered by welding 21cm DANOPOL HS 1.5 COVERSTRIP strips in the same colour.

For system application:

In the case of thermal insulation, the boards must be adhered to the substrate using DANOTHERM with a gap of no more than 1 mm between boards.
The surface of the base substrate shall be resistant, uniform, smooth, clean, dry, and free of foreign bodies.
Before laying the waterproofing membrane, apply Fleecebond Adhesive to the entire surface of the substrate or insulation board in accordance with the applicable datasheet instructions.
Mount the film on the vertical surface without the need for adhesive.

Presentation

Length (cm): 1500
Length measurement standard: EN 1848-2
Width (cm): 180
Width measurement standard: EN 1848-2
Thickness (mm): 1,5
Colour: Anthracite
Product code: 210312

Technical Data

Concept	Value	Standard
Mass per unit area (nominal) (kg/m²)	2.2	-
Longitudinal elongation at break (%)	> 50	-
Transversal elongation at break (%)	> 60	-
External fire behaviour	Froof	EN 13501-5
Longitudinal & transversal dimensional stability	< 0.3	EN 1107-2
Water vapour permeability (µ)	20.000 ± 30%	EN 1931
Flexibility at low temperature (ºC)	< -30	EN 495-5
Reaction to fire	E	EN 13501-1
Resistance to static loading (kg)	> 60	EN 12730 Método B
Resistance to root penetration	Pasa	EN 13948
Longitudinal & transversal tensile strength (N/5cm)	> 1500 / > 1300	EN 12311-2 Método A
Longitudinal resistance to tearing (nail shank) (N)	> 400	EN 12310-2
Transversal resistance to tearing (nail shank) (N)	> 400	EN 12310-2
Resistance to impact, A (mm)	> 800	EN 12691
Overlaps resistance (Shear of overlaps) (N/50mm)	> 1200	EN 12317-2
Overlaps resistance (Peeling of overlap) (N/50mm)	> 300	EN 12316-2
Hazardous substances	NPD	-
Emissivity	0,86±0,02	ASTM C1371-04a(2010)e1

Addtitional Technical Data

Nominal minimum thickness 1.5 (-5%; +10%) EN 1849-2 Mass (kg/m²) 2.2 (-5%; +10%) EN 1849-2 Loss of elongation at break (UV 5000 h) < 10< 10 EN 1297, EN 12311-2EN 1297, EN 12311-2 Loss of plasticizers (mass change at 30 days) (%) < 4.5 EN ISO 177 Flatness (mm) < 10 EN 1848-2 Nominal minimum thickness 1.5 (-5%; +10%) EN 1849-2 Mass (kg/m²) 2.2 (-5%; +10%) EN 1849-2 Loss of elongation at break (UV 5000 h) < 10< 10 EN 1297, EN 12311-2EN 1297, EN 12311-2 Loss of plasticizers (mass change at 30 days) (%) < 4.5 EN ISO 177 Flatness (mm) < 10 EN 1848-2 Straightness (mm) < 50 EN 1848-2 Hail resistance (soft Support) (m/s) 50 - Hail resistance (hard support) (m/s) 28 EN 13583-2012